How to increase the brightness of ABS plastic injection products


First, injection mold
1. If the mold cavity is not processed well, if there are scars, micro holes, wear, roughness, etc., it will inevitably reflect on the plastic part, making the plastic part poor in gloss. In this regard, the mold must be carefully processed to make the surface of the cavity Small roughness, polishing chrome plating if necessary.
 2. If the surface of the cavity has oil stains, water stains, or too much release agent, the surface of the plastic part will be dark and dull. In this regard, you should remove the oil stains and water stains in time, and limit the use of mold release agents.
3. If the demolding angle of the plastic part is too small, it is difficult to demold, or the force is too large during demolding, so that the surface gloss of the plastic part is the best. In this regard, the demolding angle of the plastic part should be increased.
4. If the mold exhaust is poor, too much gas stays in the mold, which also causes poor gloss. For this, check and correct the mold exhaust system.
5. If the cross-sectional area of the gate or runner is too small or changes abruptly, the melt will be subjected to too much shear force when flowing in it, which will cause turbulent dynamic flow, resulting in poor gloss. For this reason, the gate and runner should be appropriately enlarged. Cross-sectional area.Second, the injection molding process
1. If the injection speed is too small, the surface of the plastic part is not dense, and the gloss is poor. In this regard, the injection speed can be appropriately increased.
2. For thick-walled plastic parts, if the cooling is not sufficient, the surface will become fluffy and the gloss will be dark. For reason, the cooling system should be improved.3. If the holding pressure is insufficient and the holding time is short, the density of the plastic part is insufficient and the gloss is poor. In this regard, the holding pressure and the holding time should be increased.4. If the melt temperature is too low, the fluidity is poor, and it is easy to cause poor gloss. Therefore, the melt temperature should be appropriately increased.
5 For crystalline resins, such as plastic parts made of PE, PP, POM, etc., uneven cooling will cause poor gloss. For this reason, the cooling system should be improved to uniformly cool.
 6. If the injection speed is too large and the cross-sectional area of the gate is too small, the vicinity of the pouring product will be dark and poor in gloss. For this reason, the injection speed and the cross-sectional area of the gate can be appropriately reduced.
Grandshine offers plastic injection molding for special project and OEM/ODM product solution.www.grashine.com

Labels:

Comments

Post a Comment

Popular posts from this blog

How to select to phone case that is fit for you

We don’t pay the insurance for our phone, but we will add some extra protection for it ， a phone case is one of the protection for your phone .So what case should we select for our smartphone ? When it comes to buying the case for our phone, we have met some problems more or less, such as “It scratches very easy” "The buttons are way to stiff when using this cases" "The color is   beautiful and it’s easy to pop on but the material is NOT durable.” Actually, most of these problems are related to the material that the phone case is made from, every material has its own advantage and disadvantage,after we know the performance of the material, we can choose a better case that is fit for you. Silicone phone case: Silicone phone case is a typical application of silicone protective cover. It’s softness is   between 35-80A Shore hardness and a slightly slippery feel . It has been popular in the market for many years. Silicone rubber, commonly known as silica gel, is a h...
Post a Comment
Read more

The five major technology changes in mobile phone shells must be known (Part 2)

3.IML technology The outstanding features of in-mold insertinjection molding (IML) technology are: the surface is a hardened transparent film, the middle is a printed pattern layer, and the back is a plastic layer. Because the ink is sandwiched between, the product can prevent the surface from being scratched and resistant. It can rub and keep the color vivid for a long time. IML technology production process: IMLtechnolog y product effect: 1）   Diversification of printing appearance effects: By combining soft-touch transfer printing with printing technologies such as color and electroplating, various appearances can be realized. 2 ） The research and development of ultra-thin IML, the thinnest can reach 0.80mm, and the deformation is less than 0.5mm; the deformation of 6-inch battery cover is less than 1.0mm; the thickness of local glue reduction can be 0.6mm. development trend: In the existing equipment and process flow of IML technolog...
Post a Comment
Read more

Why will TWS become the mainstream of headphones?

What are TWS Bluetooth headsets? Why is TWS headsets a lifestyle in addition to wearable? From a macro perspective, wireless and multi-device collaboration is the mega trend. On the micro level, the arrival of Bluetooth 5.0 has enabled TWS headsets to be upgraded with the underlying technology; global smartphones have gradually eliminated the headphone jack, which has accelerated the development of TWS headsets. The emergence of TWS headphones can be said to be a necessity. TWS headsets are not accepted by consumers and the market from the beginning. There are many problems such as battery life, transmission, sound quality, and price, which have not been completely resolved so far. As more and more consumers begin to pay attention to TWS headsets, demands such as voice assistants, health monitoring, and noise reduction modes also begin to emerge. TWS will become the mainstream of mobile phones in the future.Why? 1, AirPods have sparked the TWS craze, As we known, the Air...
Post a Comment
Read more